Highly Electroconductive Nanopapers Based on Nanocellulose and Copper Nanowires: A New Generation of Flexible and Sustainable Electrical Materials.

Nowadays, the development of sustainable high-performance functional nanomaterials is in the spotlight. In this work, we report the preparation of a new generation of flexible and high electroconductive nanopapers based on nanofibrillated cellulose (NFC) and copper nanowires (CuNWs). Homogeneous red brick color nanopapers (thickness 30.2-36.4 µm) were obtained by mixing different amounts of NFC aqueous suspensions and CuNWs (1, 5, 10, 20, and 50 wt %), followed by vacuum filtration and drying. scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) analysis confirmed the incorporation of the different amounts of CuNWs, and their uniform and random distribution. All of the nanomaterials displayed good mechanical properties, viz., Young's modulus = 2.62-4.72 GPa, tensile strength = 30.2-70.6 MPa, and elongation at break = 2.3-4.1% for the nanopapers with 50 and 1 wt % of CuNWs mass fraction, respectively. The electrical conductivity of these materials strongly depends on the CuNW content, attaining a value of 5.43 × 104 S·m-1 for the nanopaper with a higher mass fraction. This is one of the highest values reported so far for nanocellulose-based conductive materials. Therefore, these nanopapers can be seen as an excellent inexpensive and green alternative to the current electroconductive materials for applications in electronic devices, energy storage, or sensors.

Nanocomposite Polymeric Materials Based on Eucalyptus Lignoboost® Kraft Lignin for Liquid Sensing Applications.

This study reports the synthesis of polyurethane-lignin copolymer blended with carbon multilayer nanotubes to be used in all-solid-state potentiometric chemical sensors. Known applicability of lignin-based polyurethanes doped with carbon nanotubes for chemical sensing was extended to eucalyptus LignoBoost® kraft lignin containing increased amounts of polyphenolic groups from concomitant tannins that were expected to impart specificity and sensitivity to the sensing material. Synthesized polymers were characterized using FT-MIR spectroscopy, electrical impedance spectroscopy, scanning electron microscopy, thermogravimetric analysis, and differential scanning calorimetry and are used for manufacturing of all solid-state potentiometric sensors. Potentiometric sensor with LignoBoost® kraft lignin-based polyurethane membrane displayed theoretical response and high selectivity to Cu (II) ions, as well as long-term stability.